Wear properties

Nylon possesses superb wear-resistant properties, making it suitable for numerous applications.
Nylon is an excellent self-lubricant, eliminating the need to apply lubricants under normal conditions. However, the use of a lubricant is recommended in applications entailing high loads or high-speed rotation. Water and other liquids will act as a lubricant on working surfaces. Keep in mind, however, that aqueous lubricants generally have high frictional coefficients.
The different grades of nylons have very similar frictional coefficients.
Abbildung 41 shows the change in frictional coefficient as a function of load and lubrication conditions.

Abbildung 41: Change in frictional coefficients as a function of load and lubrication conditions
(sliding speed 14m/min)

Table 8 shows the relationship between the amount of friction and the frictional coefficient when nylon 66 is used as a bearing in conjunction with a variety of different materials and lubricants.

Unlike metal, which wears in at a relatively constant rate over time, wear in nylon progresses at a rapid rate initially. Abbildung 42 shows an example comparing the wear behavior of a nylon bearing to that of a sintered bronze bearing.

Abbildung 42: Wear behavior of sintered bronze and nylon bearings

The frictional coefficient and state of wear in nylon also differs depending on surface crystallinity. Heat treatment after injection molding will advance crystallinity and result in a lower frictional coefficient and less wear. Abbildung 43 shows the effect of heat treatment on the frictional properties of nylon.
Adding molybdenum dioxide or graphite to nylon improves the frictional properties of nylon. Not only do these substances act as solid lubricants, but it is believed they also act as nucleating agents and cause the development of fine crystals in tight formation. Abbildung 44 shows the effects of adding molybdenum dioxide to nylon 66.
Abbildungs 45 and 46 show the effects of adding molybdenum dioxide or graphite to nylon. As you can see, a small amount of molybdenum dioxide results in a significant effect.

• Abbildung 43: Nylon frictional properties
• Abbildung 44: Effects of molybdenum dioxide additive
  on friction with nylon 66 (slide speed: 48.8m/min)

• Abbildung 45: Load dependence of frictional coefficient
  of nylon 6 with additive
• Abbildung 46: Load dependence of amount of wear
  in nylon 6 with additive